Water insoluble antibiotic metal cellulose compounds and process of preparation

ABSTRACT

A process for the preparation of a water insoluble antibiotic which process comprises reacting at pH 3 to 7 an antibiotic exhibiting antibacterial activity with a titanium, tin, zirconium, iron or vanadium derivative of cellulose or a derivative thereof. The antibiotic may be streptomycin, paromomycin, gentamycin, kanamycin, neomycin, polymyxin, ampicillin or natamycin.

' United States Patent 1191 Barker et al.

[ WATER INSOLUBLE ANTIBIOTIC METAL CELLULOSE COMPOUNDS AND PROCESS OF PREPARATION [75] Inventors: Sidney Alan Barker; John Frederick Kennedy, both of Birmingham, England [73] Assignee: Ranks Hovis McDougall Limited,

London, England [22] Filed: Apr. 27, 1973 [21] Appl. No.: 354,958

[30] Foreign Application Priority Data Ma 3. 1972 United Kingdom 20617/72 [52] US. Cl. 260/210 AB; 260/210 K; 260/210 NE; 260/210 S; 260/212 R; 424/180 [51] Int. Cl. C0711 15/22 [58] Field of Search... 260/209 R. 210 AB. 210 NE. 260/210 K. 212 R. 210 S [56] References Cited UNITED STATES PATENTS 2.489.651 l 1/1949 Langkammerer 260/212 Nov. 11, 1975 2.562.955 8/1951 Schuyten et al. 260/212 2.702.228 2/1955 Kahler et a1. 260/212 2.811.481 10/1957 Chornock 260/210 NE 2.830.011 4/1958 Parker et a1 260/210 NE 2.931.798 4/1960 Umezawa et a1 260/210 K 3.074.927 1/1963 Saltman et al. 260/209 R 3.563.978 2/1971 Ochs 260/209 R 3.607.864 9/1971 Halpem 260/210 NE 3.691.151 Guadagnini et 260/210 K Primary Eruminer-Johnnie R. Brown Attorney, Agent. or FirmStevens. Davis. Miller & Mosher 1 1 ABSTRACT 12 Claims, N0 Drawings WATER INSOLUBLE ANTIBIOTIC METAL CELLULOSE COMPOUNDS AND PROCESS OF PREPARATION This invention is for improvements in or relating to antibiotics and has particular reference to the modification of antibiotics by attachment to water insoluble solid matrices, i.e. cellulose or a derivative thereof.

More particularly this invention relates to methods for the water insolubilization of antibiotics exhibiting antibacterial activity by attachment to certain derivatives of cellulose in such a way that the insolubilized antibiotics retain part of the spectrum of biological activ ity normally exhibited by them in solution. They thereby afford protection to the cellulose derivatives against attack by those particular micro-organisms. Such insolubilized antibiotics have applications in providing selective protection against microbial attack on paper and legal documents, canvas, chromatographic fillings of columns where these are based on cellulose derivatives, insolubilized enzyme reactors based on attachment of the enzyme to cellulose derivatives, protection of certain cellulose based packings for cooling towers and wall papers based on cellulose. They also provide a novel form of sterility for sheets and other cotton based fabrics and gauze and can be useful as wound dressings particularly for burns prone to infection by Pseudomonas aeruginosa or for treating infected root canals in teeth prior to root filling.

Antibiotics are well known to exhibit antimicrobial activity in solution even at low concentrations. Although it is difficult to predict prior to their preparation and testing, it has also been established that a limited number of derivatives of antibiotics are also biologi cally active in solution. What is unexpected is that certain antibiotic preparations rendered insoluble by attachment to cellulose still exhibit part, but in general not all, of the normal antimicrobial activity of the original soluble antibiotic even when the said preparations have been extensively washed with water and strong salt solutions. A limited number of insoluble antibiotic preparations have been provided which inhibit the growth of all four organisms under test namely Streptococcus faecah's, Staphylococcus pyogenes, Escherichia coli, and Pseudomonas aeruginosa.

A method has been devised for antibiotic insolubilization based on a technique in which a titanium, tin, zirconium, iron or vanadium derivative of cellulose is chemically coupled to an antibiotic.

The invention provides antibiotics attached to water insoluble solid matrices.

It is a particular object of this invention to provide active water-insoluble preparations of antibiotics exhibiting antibacterial activity chemically coupled with organo-metallic derivatives of cellulose or a derivative thereof.

The present invention provides water insoluble derivatives of streptomycin, paromomycin, gentamycin, kanamycin, neomycin, polymyxin, ampicillin and natamycin chemically coupled to titanium, tin, zirconium,

iron or vanadium derivatives of cellulose or a derivative thereof.

According to the present invention there is also provided a process for the preparation of a water insoluble antibiotic which process comprises reacting at pH 3 to 7 an antibiotic exhibiting antibacterial activity with a titanium, tin, zirconium, iron or vanadium derivative of cellulose or a derivative thereof.

The organo-metallic derivative of cellulose or a derivative thereof may be obtained by reaction of the cellulose or a derivative thereof with a salt or other derivative of titanium, tin, zirconium, iron or vanadium that gives a suitable organo-metallic derivative.

The reaction may be carried out at'a pH of 4.5 for 1 hour at 4C.

The antibiotic exhibiting antibacterial activity preferably contains at least one amino group; normally one or more primary amino groups is present.

Antibacterial bioassays were employed to assess the effectiveness of the preparations. Since the samples of the antibiotics attached to cellulose were water-insoluble, a modification of the usual method of stepwise dilution was adopted. In addition, a constant weight 15 mg) of the sample was tested each time in order to provide results which allowed comparisons to be drawn.

Each antibiotic is optimally coupled via a particular metal derivative of cellulose to obtain maximum antimicrobial activity.

Thus from the results given in Tables 1 to 5 the following antibiotics exhibit a decreasing order of antibacterial activity from the first mentioned metal salt used for coupling to cellulose to the last in each series.

Streptomycin: SnCl, ZrCL, TiCl VCl FeCl Paromomycin: SnCl, FeCl ZrCl, TiCl UCl Gentamycin: SnCl ZrCl, TiCl FeCl VCl Kanamycin: SnCl ZrCl FeCl TiCl VCl Neomycin: ZrCl; I SnCl, FeCl VCl TiCl Polymyxin: FeCl VCl SnCl, ZrCl TiCl Ampicillin: SnCl, FeCl VCI TiCl ZrCL, Natamycin: SnCl VCl FeCl ZrCl or TiCl These orders of antibacterial activity were assessed from their action against two gram positive and two gram negative bacteria. The above orders of activity, therefore give the preferred methods by which the antibiotic is coupled to cellulose. Where two methods of coupling are apparently equally effective, the least toxic and cheapest metal is the method preferred. For particular uses, other factors such as its ability to inhibit the growth of Pseudomonas aeruginosa in a burns dressing are decisive. In particular the following were effective against all four test organisms.

Streptomycin tin cellulose derivative Streptomycin zirconium cellulose derivative Paromomycin tin cellulose derivative Gentamycin tin cellulose derivative Gentamycin titanium cellulose derivative zirconium cellulose derivative Kanamycin tin cellulose derivative Kanamycin zirconium cellulose derivative Neomycin zirconium cellulose derivative Neomycin tin cellulose derivative Natamycin tin cellulose derivative Following is a description by way of example of methods of carrying the invention into effect. General Information and Procedures of Testing Sources ofAntibiotics. Streptomycin sulphate (Glaxo Laboratories Ltd.), neomycin sulphate (Boots Pure Drug Co. Ltd.), kanamycin sulphate (Bayer), paromomycin sulphate (Parke-Davis Ltd), gentamycin sulphate (Aspro- Nicholas Ltd.), ampicillin (Beecham Research Lab.),

polymyxin B sulphate (Burrough Wellcome and Co.) and natamyein (Arthur H. Cox and Co. Ltd.).

Bioassay methods. (a) An ri-baclerial assay. Antibacterial bioassay was performed using two gram positive (Streptococcus faecalis and Staphylococcus pywgenes) and two gram negative (Escherichia culi and Pseudomonas aeruginosa) bacteria as representative organisms. A circular nutrient agar plate (8.7 cm diameter) was freshly prepared from sterile. melted and cooled nutrient agar and a ditch 1.2 cm) cut out along the diameter of the plate. A suspension of the test material mg) in the same agar was poured into the ditch and pure cultures of the four organisms were streaked across the ditch. The plate was then incubated at 37C. for 24 hours. The extent of inhibition to growth of each organism was measured from the edge of the ditch. Control plates without the samples were set up at the same time to check the growth of the organisms. Standards of the pure'antibiotics were similarly tested.

EXAMPLE 1 Microcrystalline cellulose ("Sigmacell", type 38; Sigma Chemical Company) g.) was mechanically stirred with filtered titanous chloride (B.D.H.. C 12.5% w/v. 200 ml). The solid was filtered off, and held for 24 hours in an oven at 45C., ground to a powder and stored at room temperature in a desiccator over phosphorous pentoxide.

Samples of the resulting titanium derivative of cellulose (l500 mg.) were washed twice with 0.02M phosphate buffer pH 5.1. The samples were then magnetically stirred with a solution of antibiotic (100 mg.) in 0.1M sodium phosphate buffer pH 4.5 ml.) for 1 hour at 4C. The insoluble material was washed with five cycles of 0.1M sodium phosphate buffer pH 5.1 (30 ml.) followed by 0.5M sodium chloride in 0.1M sodium phosphate buffer pH 5.1 (30 ml.). The samples were then suspended in 0.1 M sodium phosphate buffer pH 5.1 (30 ml.) and dialyzed against running tap water overnight. The final volume of each suspension was adjusted to 30 ml. prior to testing. For results see Tables 1 and 2.

TABLE 1 Coupling of titanium derivative of cellulose with antibiotics Product from inhibition to Titanium- Slrcplu- Slaphylucellulose Escherichia coccus coccus Pscmlomunas and: coli fiiccalis pyvgcncs aeruginuxa Streptomycin 7mm from 5mm 4mm from from sulphate ditch ditch ditch Paromomycin 5mm from 5mm from sulphate ditch ditch Gentamycin 5mm from across 5mm across from sulphate ditch ditch ditch ditch Kanamycin 5mm from 7 across 5mm from sulphate ditch ditch ditch TABLE 2 Coupling of titanium derivative of cellulose with antibiotics Product from inhibition to Titanium- Slrcpro- Smphylocellulose Escherichia cuccus cuccus Pselldumunas and: coli fuccalis pyugenes aeruginusa Neomycin across across sulphate ditch ditch TABLE Z-continued Coupling of titanium derivative of cellulose with The procedure described in Example 1 was repeated using other metal salt solutions in place of titanous chloride. In this way iron. tin, zirconium and vanadium derivatives of cellulose were prepared using ferric chloride (A.R. grade. Hopkin and Williams Ltd., c, 12.5% w/v), stannic chloride (Hopkin and Williams Ltd., 12.5% w/v). zirconium tetrachloride (British Drug Houses Ltd.. c, 12.5% w/v). and vanadium trichloride (British Drug Houses Ltd., c, 12.5% w/v) respectively. Samples of each of the above mentioned derivatives of cellulose were contacted with solutions of antibiotic as described in Example 1 and submitted to the same procedure of washing prior to biological testing. For results'see Tables 3, 4 and 5.

TABLE 3 Comparison of antibacterial activity of antibiotics coupled to Iron. Tin. Zirconium and Vanadium Cellulose Antiinhibition to biotic Sirepw- S mphylu- Pseudoeoupled Method Escherichia cuccus cuccus mount to used coli faccali: pyvgenes aerucellulose ginosa Streptomycin FeCl across 5mm from sulphate ditch ditch SnCl 15mm 3mm 15mm 6mm from from from from ditch ditch ditch ditch ZrCl l2mm across 12mm across from from ditch ditch ditch ditch VCl 7mm from 8mm from ditch ditch Paromodimmycin FcCl 5mm from inished 7mm from across ditch across ditch ditch ditch SnCl lOmm across l0mm across from from ditch ditch ditch ditch ZrCl 9mm from across lOmm from ditch ditch ditch VCl 4mm from 5mm from ditch ditch TABLE 3 Comparison of antibacterial activity of antibiotics coupled to Iron. Tin. Zirconium and Vanadium Cellulose TABLE 3-continued Comparison of antibacterial activity of antibiotics coupled to Iron. Tin. Zirconium and Vanadium Cellulose Comparison of antibacterial activity of antibiotics coupled to Iron, Tin, Zirconium and Vanadium Cellulose Anti- Inhibition to biotic S lrep!o Staph \'I0 Pseudocouplcd Method Escherichia ('OCCHS (UCLHS nwnus to used coh' faet'alis pyugenes aeru- Cellulose ginusu Kana- FcCI 5mm from across 6mm from mycin ditch ditch ditch SnCI 12mm from 2mm 14mm from across from ditch ditch ditch ditch ZrCl l2mm from across 12mm from across ditch ditch ditch ditch VCl across 4mm from ditch ditch dimdim- Neo- FeCl 3mm from inishcd 3mm from inishcd mycin ditch across ditch across ditch ditch SnCl, 3mm from across 4mm from across ditch ditch ditch ditch ZrCl, 5mm from across 4mm from across ditch ditch ditch ditch dimdim- VCI 3mm from inished 3mm from inishcd ditch across ditch across ditch ditch TABLE 5 Comparison of antibacterial activity of antibiotics coupled to Iron, Tin, Zirconium and Vanadium Ccllulosc Anti- Inhibition to biotic Strepto- Smphylo- Pseudw coupled Method Escherichia coccus cot-cu: mona to used t'oli faeculir pyugener aerucellulose ginora Poly- FcC l across across across myxin ditch ditch ditch SnCl 3mm from across ditch ditch ZrCl 2mm from across ditch ditch VCl lmm from across across ditch ditch ditch dim- Nata- FeC l across inishcd mycin ditch across ditch dim- SnC 1 across across across inishcd ditch ditch ditch across ditch ZrCl dimdirndim- VCl inishcd inishcd inishcd across SCIOSS BCTOSS ditch ditch ditch dim- TABLE 5-continued Comparison of antibacterial activit of antibiotics coupled to Iron, Tm, ZlICOnlUm and anadlum Cellulose Anti- Inhibition to biotic Srrcplu- Slaphylv- Pram/0- coupled Mcthod Escherichia ("occur cut-cu: mom! to used rali fllfl'tl/IS pyugwu's (wrucellulose ginosu Ampi- FcCl across inishcd cillin ditch across ditch dimdimdimdim- SnCI, inishcd inishcd inishcd inishcd across across across across ditch ditch ditch ditch ZrCL,

dimdim- VCl inishcd inishcd across across ditch ditch We claim:

1. A process for the preparation of an active water insoluble antibiotic comprising reacting at a pH between 3 and 7 an antibiotic exhibiting antibacterial activity containing at least one amino group selected from the group consisting of streptomycin, paromomycin. gentamycin, kanamycin, neomycin, polymyxin, ampicillin and natamycin with a metal derivative of cellulose, said metal being selected from the group consisting of titanium, tin, zirconium, iron and vanadium.

2. A process as claimed in claim 1 wherein said titanium, tin, zirconium, iron or vanadium derivative of cellulose is obtained by reaction of said cellulose with an aqueous solution of a metal salt selected from the group consisting of halides of titanium, tin, zirconium, iron or vanadium.

3. A process as claimed in claim 1 wherein the reaction is carried out at 'a pH of 4.5 for 1 hour at 4C.

4. Active water-insoluble preparations of antibiotics exhibiting antibacterial activity containing at least one amino group selected from the group consisting of streptomycin, paromomycin, gentamycin, kanamycin, neomycin, polymyxin, ampicillin and natamycin chemically coupled to a titanate, zirconate, stannate, iron or vanadium derivative of cellulose.

5. A water insoluble derivative of streptomycin chemically coupled to a titanium, tin, zirconium, iron, or vanadium derivative of cellulose.

6. A water insoluble derivative of paromomycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

7. A water insoluble derivative of gentamycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

8. A water insoluble derivative of kanamycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

9. A water insoluble derivative of neomycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

10. A water insoluble derivative of polymyxin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

11. A water insoluble derivative of ampicillin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.

12. A water insoluble derivative of natamycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose. 

1. A PROCESS FOR THE PREPARATION OF AN ACTIVE WATER INSOLUBLE ANTIBIOTIC COMPRISING REACTING AT A PH BETWEEN 3 AND 7 AN ANTIBIOTIC EXHIBITING ENTIBACTERIAL ACTIVIY CONTAINING AT LEAST ONE AMINO GROUP SELECTED FROM THE GROUP CONSISTING OF STREPTOMYCIN, PAROMOMYCIN, GENTAMYCIN, KANAMYIC, NEOMYCIN, POLYMYXIN, AMPICILLIN AND NATAMYCIN WITH A METAL DERIVATIVE OF CELLULOSE, SAID METAL BEING SELECTED FROM THE GROUP CONSISTING OF TITANIUM, TIN, ZIROCONIUM, IRON AN VANADIUM.
 2. A process as claimed in claim 1 wherein said titanium, tin, zirconium, iron or vanadium derivative of cellulose is obtained by reaction of said cellulose with an aqueous solution of a metal salt selected from the group consisting of halides of titanium, tin, zirconium, iron or vanadium.
 3. A process as claimed in claim 1 wherein the reaction is carried out at a pH of 4.5 for 1 hour at 4*C.
 4. Active water-insoluble preparations of antibiotics exhibiting antibacterial activity containing at least one amino group selected from the group consisting of streptomycin, paromomycin, gentamycin, kanamycin, neomycin, polymyxin, ampicillin and natamycin chemically coupled to a titanate, zirconate, stannate, iron or vanadium derivative of cellulose.
 5. A water insoluble derivative of streptomycin chemically coupled to a titanium, tin, zirconium, iron, or vanadium derivative of cellulose.
 6. A water insoluble derivative of paromomycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 7. A water insoluble derivative of gentamycin chemically coUpled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 8. A water insoluble derivative of kanamycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 9. A water insoluble derivative of neomycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 10. A water insoluble derivative of polymyxin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 11. A water insoluble derivative of ampicillin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose.
 12. A water insoluble derivative of natamycin chemically coupled to a titanium, tin, zirconium, iron or vanadium derivative of cellulose. 